Basic Info.
Model NO.
ABS-HMG47MDXH
EINECS
618-371-8
Material
Acrylonitrile-Butadiene-Styrene Copolymers/ABS
Usage
General Plastics, Engineering Plastics, Specialty Plastics
Plastic Properties After Heated
Thermoplastic Plastics
Plastic Forming Method
Injection
Color
White
Place of Origin
Guangdong, China
Use
Radiator Front Cover.Automotive Parts
Features
Lubricated, Good Wear Resistance, Low Friction and
Application
Zippers Irish Flutes, Bagpipes, Practice Chanters
Form
Resin Pellets
Delivery Time
in 7 Days
Transport Package
Bag
Specification
25KG
Trademark
Forever
Origin
China
HS Code
390740000
Production Capacity
50000t/Year
Packaging & Delivery
Package Size
75.00cm * 55.00cm * 15.00cm
Package Gross Weight
25.010kg
Product Description
Modified ABS High Flow Grade Grade Extrusion Molding Jet black High flow https://forever-plastics.en.made-in-china.com/product-list-1.html
Product Description
| General | ||||||
| Form | Resin Pellets | |||||
Feature | Biocompatible Fda | Medical Disinfection Application X-Ray Sterilizable | Gamma Sterilizable Eto Sterilization | |||
| Appliances | Electronic Displays | Fluid Handling | ||||
| Usage | Lawn And Garden Equipment | Pharmaceuticals | Outdoor | |||
| Physical | Nominal Value | Test Method | ||||
| Density / Specific Gravity | 1.05 g/cm³ | |||||
| Melt Mass-Flow Rate, MFR | ||||||
| 230 °C;3.8 kg | 5.6 g/10min | ASTM D1238 | ||||
| 220 °C;10 kg | 19 g/10min | ISO 1133 | ||||
| Molding Shrinkage, Flow(3.2 | mm) | 0.50 - 0.80 % | Internal Method | |||
| Mechanical | Nominal Value | Test Method |
| Tensile Modulus | ||
| 5 mm/min | 2270 MPa 2530 MPa | ASTM D638 ISO 527-2/1 |
| Tensile Strength, Yield | ||
| 5 mm/min;Type I | 44.0 MPa 50.0 MPa | ASTM D638 ISO 527-2/5 |
| Tensile Strength, Break | ||
| 5 mm/min;Type I | 33.0 MPa 35.0 MPa | ASTM D638 ISO 527-2/5 |
| Tensile Elongation, Yield | ||
| 5 mm/min;Type I | 2.0 % 2.6 % | ASTM D638 ISO 527-2/5 |
| Tensile Elongation, Break | ||
| 5 mm/min;Type I | 24 % 25 % | ASTM D638 ISO 527-2/5 |
| Flexural Modulus | ||
| 1.3 mm/min;50 mm;Span | 2340 MPa | ASTM D790 |
| 2 mm/min | 2410 MPa | ISO 178 |
| Flexural Stress, at Yield(2 mm/min) | 76.0 MPa | ISO 178 |
| Flexural Stress, Yield(1.3 mm/min;50 mm;Span) | 72.0 MPa | ASTM D790 |
| Notched Izod Impact | ||
| -30 °C | 130 J/m | ASTM D256 |
| 23 °C | 320 J/m | ASTM D256 |
| 80*10*4 mm;-30 °C | 8.0 kJ/m² | ISO 180/1A |
| 80*10*4 mm;23 °C | 23 kJ/m² | ISO 180/1A |
| Instrumented Dart Impact, Total Energy(23 °C) | 30.0 J | ASTM D3763 |
| Thermal | Nominal Value | Test Method |
| Deflection Temperature Under Load, Unannealed | ||
| 0.45 MPa;3.2 mm | 94.0 °C | ASTM D648 |
| 1.8 MPa;3.2 mm | 80.0 °C | ASTM D648 |
| 80*10*4 mm;1.8 MPa;4 mm;64 mm;Span | 80.0 °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||
| 50 °C/h;50 N;Rate A;Loading 2 | 98.0 °C 100 °C | ASTM D1525 ISO 306/B50 |
| CLTE, Flow(-40 - 40 °C) | 8.8E-5 cm/cm/°C | ISO 11359-2 |
| CLTE, Transverse(-40 °C) | 8.8E-5 cm/cm/°C | ISO 11359-2 |
| Processing | Nominal Value | |
| Drying Temperature<Injection> | 80 - 95 °C | |
| Drying Time<Injection> | 2.0 - 4.0 hr | |
| Suggested Max Moisture<Injection> | 0.10 % | |
| Suggested Shot Size<Injection> | 50 - 70 % | |
| Rear Temperature<Injection> | 190 - 210 °C | |
| Middle Temperature<injection> | 205 - 225 °C | |
| Front Temperature<Injection> | 215 - 240 °C | |
| Nozzle Temperature<Injection> | 220 - 260 °C | |
| Processing Temp, Melt<Injection> | 220 - 260 °C | |
| Mold Temperature<Injection> | 50 - 70 °C | |
| Back Pressure<Injection> | 0.300 - 0.700 MPa | |
| Screw Speed <Injection> | 30 - 60 rpm | |
| Vent Depth <Injection> | 0.038 - 0.051 mm |
| Product Description | ||||
| A semi-conductive grade of acetal copolymer for applications requiring rapid dissipation of static build- up. | ||||
| General | ||||
| Form | Resin | Pellets | ||
| Physical | Nominal Value | Test Method | ||
| Density / Specific Gravity | 1.40 g/cm³ | |||
| Water Absorption | 0.21 % | ASTM D570 | ||
| Moisture Absorption at Equilibrium | 0.80 % | ASTM D570 | ||
| Linear Mold Shrinkage | 2.2 % | |||
| Linear Mold Shrinkage, Transverse | 1.8 % | |||
| Hardness, Rockwell R | 111 | ASTM D785 | ||
| Mechanical | Nominal Value | Test Method | ||
| Tensile Strength, Yield | 37.0 MPa | ASTM D638 | ||
| Elongation at Break | 30 % | ASTM D638 | ||
| Flexural Strength | 52.0 MPa | ASTM D790 | ||
| Flexural Modulus | 2100 MPa | ASTM D790 | ||
| Compressive Strength | 66.0 MPa | ASTM D695 | ||
| Shear Strength | 40.0 MPa | ASTM D732 | ||
| Izod Impact, Notched Temperature; 23 °C Temperature; -29 °C | 50 J/m 30 J/m | ASTM D256 | ||
| Thermal | Nominal Value | Test Method | ||
| Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa | 152 °C 106 °C | ASTM D648 | ||
| Flammability, UL94 | HB | UL 94 | ||
Dongguan FOREVER Co., Ltd. Was founded in 2005 and is a national high-tech enterprise and national-level specialized giant enterprise dedicated to the research and production of polymer composite modified materials. With an annual capacity of 100, 000 tons of modified engineering plastics. Since its establishment, the company has been committed to the research of high-performance composite materials such as modified PC, PC/ABS, PBT, PA6, etc. Its products have been widely used in industries such as LED lighting, consumer electronics, new energy, security equipment, and small household appliances, providing customers with efficient delivery experience, ultimate price advantages, and strict quality assurance, contributing to the creation of a green and environmentally friendly world.
Dongguan FOREVER Co., Ltd's main products has obtained UL certification for RTI authorized temperature, outdoor weather resistance F1 and 5VA flame retardancy grades, as well as recycled-certified post-consumer low-carbon circulation products. Dongguan FOREVER Co., Ltd's products are highly recognized by customers worldwide for their reliable quality, excellent performance, and superior cost-effectiveness.
With a strong focus on research and development, Dongguan FOREVER Co., Ltd. Has established an advanced technology research and development center, equipped with state-of-the-art testing and analysis equipment and a professional R&D team that has accumulated rich experience in the field of polymer composite modified materials. Dongguan FOREVER Co., Ltd also maintains close partnerships with renowned universities and research institutions to stay at the forefront of technology and drive innovation in the industry.